Thank you for your advice and suggestion! as Weldstan said, It's decided to use 304L with E318. Thank you

@metengr Thank you very much! If you could give further help, can I learn what code/practice it is stated?

Hello! I have a problem dealing with what material to choose as written in the title I need to urgently purchase materials for full welding stiffener ring on the pipe, while pipe material is SS316Ti. to reduce delivery impact, I want to change the material of stiffener ring to SS304 or SS316...

Hello! I have a problem dealing with what material to choose as written in the title I need to urgently purchase materials for full welding stiffener ring on the pipe, while pipe material is SS316Ti. to reduce delivery impact, I want to change the material of stiffener ring to SS304 or SS316...

It's ASME 31.3

Hi. there's this problem found at welding shop, as mentioned in title, we have overlapping seam problem. For further info. the material is SS316Ti, Wall thickness is 22.23mm the design condition of pipe is 3.5 BarG and 515'C The longitudinal seam is heat treated by manufacturer. Is it okay to...

I'm designing Furnace transfer line to crude column The design Temp. is 390 degrees C and The designed material of the line is SS316Ti. I found our pipe fitting vendor shipped one of the elbows with SS321. Please give me a clue if it's okay to use in terms of both the design condition-wise and...