The following is the compositional differences between
1100 and 1200:
1100
.95Si+Fe, .05-.2Cu, .05Mn, .10Zn, .05others
1200
1.0Si+Fe, .05Cu, .05Mn, .10Zn, .05Ti, .05others
Vince
If welding in the T6 condition, you will loose properties
in and around the weld area. The properties in the welded area will be comparable to those in the annealed condition.
In addition, when welding in T6 (if welding is significant)you may induce stress which may result in cracks.
In...
I need some information on welding 430 (or 430F)
stainless steel to 304 or 316.
Is it possible using TIG, beam or laser welding?
What are the concerns when welding these materials
together if any?
What filler rod is recommneded?
Any other information would be greatly appreciated
Thank You...
I need some information on welding 430 (or 430F)
stainless steel to 304 or 316.
Is it possible using TIG, beam or laser welding?
What are the concerns when welding these materials
together if any?
What filler rod is recommneded?
Any other information would be greatly appreciated
Thank You...
I need some information on welding 430 (or 430F)
stainless steel to 304 or 316.
Is it possible using TIG, beam or laser welding?
What are the concerns when welding these materials
together if any?
What filler rod is recommneded?
Any other information would be greatly appreciated
Thank You...
I need some information on welding 430 (or 430F)
stainless steel to 304 or 316.
Is it possible using TIG, beam or laser welding?
What are the concerns when welding these materials
together if any?
What filler rod is recommneded?
These are just some of the questions.
Thanks
Vince Maffei