Nov 6, 2012 #1 arash807 Mechanical Aug 8, 2012 48 0 0 IR Can we use SS410 instead of 17-4-PH in a control valve which is installed in steam service?
Nov 6, 2012 #2 EdStainless Materials May 20, 2004 15,893 0 36 US for the internals? Sure you can, but it won't last as long. If the valve runs wide open it might work, but if you are throttling then there will be a huge difference in life. = = = = = = = = = = = = = = = = = = = = Plymouth Tube Upvote 0 Downvote
for the internals? Sure you can, but it won't last as long. If the valve runs wide open it might work, but if you are throttling then there will be a huge difference in life. = = = = = = = = = = = = = = = = = = = = Plymouth Tube
Nov 8, 2012 #3 Zinov New member Dec 18, 2006 44 0 0 CA Do you need mechanically stronger material than SS410 Do you need more corrosion resistant material than SS410 17-4PH;SS455C; why not SS420... Zinov Upvote 0 Downvote