ANTI Coating - problem with stickyness lubricant after drying

[AGS]

Metal parts stick to each other due to a lubricating substance. Polyethylene glycol or hydroxyethylcellulose provide the right gliding properties but cause stickiness problems when cleaning is not done properly. Is there something I can add so that the film becomes weak / cracks after drying?

 

[CorrosionX]

Hello AGS, Give me a call at 607-547-1940. I might have some info that would be helpful to you. Thanks, Matt Curpier