Antimony Black Antigalling/Lubricant
- Thread starter TEV
- Start date
I don't know if this can be used as anti-seiz material, but I would suggest to you to be carefull !!!!!.
if melting point of antimony is close to the working temperature of your working peice, then it might cause a catastrofic failure due to a Phinomenone called Lequid Metal Embretelment (LME), you can use a Nickle based anti-siez compound instead. Please read about (LME) before deciding which compound to use as an anti-siez.
if Lead,Cadmium,Zink,Merqury is in the compound then try to refraine from using it.
Also double insure that Antimony would not cause (LME) to SS before taking any further step.
Regards
if melting point of antimony is close to the working temperature of your working peice, then it might cause a catastrofic failure due to a Phinomenone called Lequid Metal Embretelment (LME), you can use a Nickle based anti-siez compound instead. Please read about (LME) before deciding which compound to use as an anti-siez.
if Lead,Cadmium,Zink,Merqury is in the compound then try to refraine from using it.
Also double insure that Antimony would not cause (LME) to SS before taking any further step.
Regards