Good afternoon, My name is Rolando and I just registered. The forum is excellent!
I bring the following doubt about the table Table 323.2.2 Requirements for low temperature toughness tests for metals ASME B31.3 2020
As we saw, it has a review in table A-3 (b) (2020) where I understand that if I have a certified welding consumable with impact test I can exempt said test in the WPS qualification, for example:
If I have a material SA-333 gr 6 with manufacturing certificate and charpy according to the standard (18 J to -45) it can be welded with a consumable E 7018 -1 factory certificate with charpy (27 J to -45)
If I use this combination in my PQR, can I waive the impact test? assuming I already have a metal base and a consumable certificate with factory impact tests? (so I interpret table 323.2.2 table A-3 does not speak of the ZAC)
greetings and thanks !
Buenas tardes, Mi nombre es Rolando y acabo de registrarme. El foro es excelente!
Traigo la siguiente duda sobre la tabla Table 323.2.2 Requirements for Low Temperature Toughness Tests for Metals ASME B31.3 2020
Como vimos tiene una revisión en el cuadro A-3 (b)(2020) donde entiendo que si tengo un consumible de soldadura certificado con prueba de impacto puedo eximir dicha prueba en la calificación de WPS, por ejemplo:
Si tengo un material SA-333 gr 6 con certificado de fabrica y charpy según norma (18 J a -45) puede ser soldado con un consumible E 7018-1 certificado de fabrica con charpy (27 J a -45)
Si uso esta combinación en mi PQR puedo eximir de hacer la prueba de impacto? asumiendo que ya tengo metal base y consumible certificado con pruebas de impacto de fabrica?. (por lo que interpreto la tabla 323.2.2 cuadro A-3 no habla del ZAC)
saludos y gracias!!