Alloy 6262 will have poor extrudability. It is an alloy created for good machinability (lots of second phase particles for initiation of ductile fracture), hence it will have poor formability. I'm not even sure how you would obtain billet stock, since this is sold as cold-finished bars in the T6, T8, or T9 conditions from companies like Alcoa.