lime calcium chloride blend

[siretb]

Hi
Solids, some humidity present in atmosphere .? about 15% huimidy volume% in above atmosphere)

Would a blend of clacium chloride (CaCl2,6H2O) 70% wt and lime (Ca(OH)2 30% corrode carbon steel at 70°C

 

[cap1a79]

If the level of calcium chloride is 70 %, definitely CS is not suitable while lime water (Calcium hydroxide) is not corrosive. Refer to the below.

https://www.materials.sandvik/en/materials-center/corrosion-tables/calcium-chloride/

https://www.materials.sandvik/en/materials-center/corrosion-tables/calcium-hydroxide/

If you are looking for the data with calcium chloride with lime (7:3), you need specific test on your own.

Although I do not know the details but you may need to consider non-metallic coating.

Lee SiHyoung,

 

[Dhurjati Sen]

Dear siretb,

CS would develop weld cracks around 65[sup]0[/sup]C in the said service.

Regards.

DHURJATI SEN
Kolkata, India

 

[siretb]

Thank you all.
If I understand correctly, the alkalinity of the lime will not mitigate the corrosive potential of calcium chloride

 

[Dhurjati Sen]

Dear siretb,

Lime alone is capable of producing those weld cracks in CS.

Regards.

DHURJATI SEN
Kolkata, India

 

[springrise]

hi,
is that a solid powder or a water solution? If a solution, you haven't specified the concentrations.