Need input regarding should annealing be performed on 4340 hardened bars? 4340 bars after heat treating at 1525F/oil quench/ tempered at 1190F. Hardness lower than 28hRC. IS full anneal required prior to rehardening and tempering at temperatures around 1125-1140F.