I have just completed a Super Duplex PQR and there is a 2" long area where there is some heat tinting. The rest of the root look great.
This test coupon has to undergo G48 Method A corrosion testing. Would there be any advantage or disadvantage to grinding the root flush as this is what will actually happen with the production weld?