What solver do you use? There are both maxwell and magnetostatic in ANSYS WB, in that case you could apply real magnetic flux so you can analyze the B-field and magnetic flux density among many other things. If you are using e.g static structural I would concentrate in getting the reaction forces correctly applied in the material you're using (you really couldn't do much else in ss).