Hello there just stumbled across this great forum and have my first question allready. today i have been trying to repair an aluminum casting whisT im to belive is a 5% magnesium casting .. i have been trying to repair it with a 5356 5% magnesium Welding rod and using pureshield argon 99% pure gas... it seems the parent material doesnt like this does anyone have any suggestions on a better/more suitable rod/gas combination to try ?? any help would be greatly appriecated.. Darren
Eng-Tips is the largest engineering community on the Internet
Intelligent Work Forums for Engineering Professionals
-
Congratulations waross on being selected by the Eng-Tips community for having the most helpful posts in the forums last week. Way to Go!
welding ali castings.
- Thread starter darreng
- Start date
darrenG;
1.) Providing the forum with the specific Al alloy would help in your selection of filler metals.
2.) Try adding helium to your shielding, it will increase arc voltage and heat input to your Al casting. Try also preheating (not excessively) your part. How is the part being prepared prior to welding? What process are you using?
3.) Finally, what is it specifically the material "...dosen't like..."? Is it difficult to adhere filler metal to, contamination, etc.
1.) Providing the forum with the specific Al alloy would help in your selection of filler metals.
2.) Try adding helium to your shielding, it will increase arc voltage and heat input to your Al casting. Try also preheating (not excessively) your part. How is the part being prepared prior to welding? What process are you using?
3.) Finally, what is it specifically the material "...dosen't like..."? Is it difficult to adhere filler metal to, contamination, etc.