Thanks for your he reply, the blue solution we are using is called verdigris.

Trying to do a process to copper that makes it go green. Were using a blue solution that does this but it can be wiped off easily, some one else does this but wont say what he uses, and it stays on and its goes hard. We think he mixes it with something else to have this affect. Would be great to...

Thanks for the replys we don't use wire brushes to clean the surfaces they get cleaned using polishing equipment like mops polishing compounds. Then wipe down with rags and stainless cleaners.

When we make pool equipment like pool ladders other types of things we use 316L bright polished tube. Then after a time it looks like it's going rusty we think it's the chlorine that's causing the problem is there anyway of stopping it with something. We clean them down but it seems to happen...

Thanks for the reply, they want brass for fancyness,cosmetic reason it's for shops.

I'm making a brass table for a beautician's salon. The customer wants it to look satin finish. Is there any thing that can be put on that will make the brass stay the finish we make, with out it oxidizing or discolouring. The people use acetone so clear lacquer will not work, looked all over and...

Thanks for the help I have done the things you have said and I was still getting problems. In the assembly there are limit mates I had to delete one of them to make them work together it seems to work I don't get the error message. So one hinge is useing full limits and doing the work while the...

I have made a draw hinge that slides in out of it self like a cupboard door in kitchen, and I made it as an assembly. when I insert it in to another assembly I able to mate it were needed, but when I Ctrl and drag another in am only able to mate so much. what I am trying to do is make this move...

Thanks

I'm just wondering if it's possible to change a single dimension colour in a drawing not all of them . I have looked in properties and there was nothing in there, I can change the colours if I insert a note.

Thanks for the replys help me out alot.

When I develop a pattern for laser cutting full scale. Im just wondering if it's possible to scale the drawing to fit on paper to a4 paper for printing without scaling each layout individual.

Thanks for that it was the dimension I was trying to change.

Thanks for your reply, I'm trying to change a dimension not suppress apart that's why it keeps changing the other one the same or should I do it same way you have explained.

Just wondering if it's possible in a assembly to use two other assemblies the same and be able to change the configuration without it changing the other one. Wot I'm trying to do is not make another one simular, I have use the Gantt key and drag it in and saved as a copy. If anyone can help it...

The mass property gives me the coordinates but I am not sure were from, as its an assembly and there are a few origins and non seem to be close.

Thanks for the reply , I am using SW12 does that make it a problem.

Can anyone tell away of showing the centroid in a drawing I am able to bring it up in the graphics area using mass. when I use it in the graphics area I don't no were the coordinates are from and its even harder to find when I am in an assembly, it would be a great help this was possible.

When using physical dynamics is it possible to keep the movement when switch off. Thanks for your help.

Thanks for the reply its a bit difficult to explain so I will try with the help of the picture. When it is shut close the latch should move up when in contact with bracket, so it slides up the front then drop in the catch part. Then when twisted it can come apart to 45 degrees, what I want it to...