Its a pretty confined picture, if you have a better picture with more of a location on the casting to id the actually riser locations and if the casting has any amount of production the ENG.DEPT at the foundry would or should have records when the pattern was poured and SAMPLED if that is a...
I know some materials are hard to obtain and find, and if you can get some in the right material, it maybe useless because the company is not on your customers approved supplier list? One option that ive done a lot of NAVY Propulsion Fabrication with is CAST/FABRICATION. Where the fittings...
The area with corrosion does it not have to be removed and some type of NDT done to the surface before welding? The proper repair would be 316L the same material as the Tower. This would do away with all the questions being asked about code and material and weld overlay, in my opinion
Thickness is a little over 2" plus the depth of the groove walls. Has to be full penetration weld 100% RT. Heres a better view or drawing on what has to be done.
How would you go about welding this machine shop fabrication thruwall drill hole in a thin wall 904 material turbine caising. I guess the machine shop doesnt know which side is port and which side is starboard, they drilled for fabrication on the wrong side of the casting. Your thoughts on how...
I notice a couple of things, I would not have it up in the air unsupported in the middle of the casing? The way its supported now is ideal for the attachment of Tie bars without having to weld the tie bars to the casing. You would need to weld some type of plate to the tie bar to fasten them at...
May I offer up a different solution from past knowledge and experience dealing with this type of weld repair or weld build-up? I just registered on this site and not sure if I should just jump right in or not?