A number for the chemical for the welding material, you can find it in the ASME Section IX.

For Material, you shall know that have different ways for material qualification. From the ASME opinion, any one who prepare well, you can get the N certificate. Best Suggestion: you shall study your products first then you can make the decision what type nulcear ASME Certificate you will really...

I did not find it in SA-240 and SA-480. could you give me some guide.

I think the UG-11 shall be the best choice

the following case: We are the Head manufacturer, we want to apply for the ASME U stamp, we only need to apply for the U part, it means that we only need the ASME Certificate U part, How about the Demonstation Products for the joint review because we have no any design, NDE, we only do the head...

I have the question, I can not find the postfabrication strain limits and required heat treatment for the Material SA-240 316L or SA-240 304L, for example, I purchased a austenitic stainless steel plate, I want to form it into head, I can calculated forming strains, but it looks no any use...

Thank you very much for you help, I will apply for the ASME U stamp.

Dear All: I have a very special products, a gasoline Tank for the automobile, the detail data: B. Design Pressure 2,160 kPa (313 psig) C. Design Temperature 65 C (150° F) D. Minimum Design Metal -29 C (-20° F) Temperature E. Service Fluid Propane or LPG F. Specific Gravity 0.5 @ 24 C (75°F) G...

I think that the Code VIII-1 UCS-85 for the test specimens is important for you.

According to the directive, there is no any requirements for none EU company limit.

According to the ASME Code Section IX, qualification for the Welder and WPS is responsible by the Manufacturer.