Jul 13, 2009 #1 kimiagar79 Materials Jun 24, 2009 6 Hi Is It Necessary to do heat treatment for SS 304 3/4" tube after U bending?
Jul 13, 2009 #2 metengr Materials Oct 2, 2003 15,478 It depends on the service application. If you want maximum corrosion resistance, yes, a solution anneal should be performed. Upvote 0 Downvote
It depends on the service application. If you want maximum corrosion resistance, yes, a solution anneal should be performed.
Jul 13, 2009 Thread starter #3 kimiagar79 Materials Jun 24, 2009 6 thanx metengr can u guide me to some refrences? actually i know that annealing is necessary but i haven't accessing to ASM Metal handbook or any other forming refrences right now and i've to proof my claim Upvote 0 Downvote
thanx metengr can u guide me to some refrences? actually i know that annealing is necessary but i haven't accessing to ASM Metal handbook or any other forming refrences right now and i've to proof my claim
Jul 13, 2009 #4 metengr Materials Oct 2, 2003 15,478 kimiagar79; I would use ASME Boiler and Pressure Vessel Code, Section I or VIII, Div 1 as proof of claim. Upvote 0 Downvote
kimiagar79; I would use ASME Boiler and Pressure Vessel Code, Section I or VIII, Div 1 as proof of claim.
Jul 13, 2009 #5 pal1967 Mechanical Jul 13, 2009 1 I am wondering when heat treating 304 ss is necessary according to ASME Division VIII (2007)code. The final product is a ss pressure vessel. Thanks. Upvote 0 Downvote
I am wondering when heat treating 304 ss is necessary according to ASME Division VIII (2007)code. The final product is a ss pressure vessel. Thanks.
Jul 13, 2009 #6 metengr Materials Oct 2, 2003 15,478 Read UHA-44 in ASME Section VIII, Div 1 to find your answer. Upvote 0 Downvote