is f6nm steel brittle or ductile material?
Eng-Tips is the largest engineering community on the Internet
Intelligent Work Forums for Engineering Professionals
-
Congratulations waross on being selected by the Tek-Tips community for having the most helpful posts in the forums last week. Way to Go!
is f6nm steel brittle or ductile ma
- Thread starter aminishfaq
- Start date
- Status
EdStainless
Materials
At what C level? What strength? What temperature?
In general this a fairly tough material but it has its limits.
= = = = = = = = = = = = = = = = = = = =
P.E. Metallurgy, Plymouth Tube
In general this a fairly tough material but it has its limits.
= = = = = = = = = = = = = = = = = = = =
P.E. Metallurgy, Plymouth Tube
Guest
It will be somewhere in between; precisely where depends on the quality and the heat treat condition.
No metallic alloy is truly 'brittle', metals just have varying degrees of ductility.
"Everyone is entitled to their own opinions, but they are not entitled to their own facts."
No metallic alloy is truly 'brittle', metals just have varying degrees of ductility.
"Everyone is entitled to their own opinions, but they are not entitled to their own facts."
Dhurjati Sen
Materials
Dear aminishfaq,
You must have found f6nm from some code. Check the UTS, Y.S., Elongation, ROA from the same.
You will get a fairly good idea about the steel.
Regards.
DHURJATI SEN
You must have found f6nm from some code. Check the UTS, Y.S., Elongation, ROA from the same.
You will get a fairly good idea about the steel.
Regards.
DHURJATI SEN