Austempered Ductile Iron

Status
Not open for further replies.
UconnMaterials

UconnMaterials

Materials
Jun 20, 2008
35
Hello,

We have a batch of austempered ductile iron, but the cross-section doesn't look like ausferrite. This image is at 1000x and the etchant is suoer picral. Could this be bainite? The hardness is 27-29 HRC. It's also brittle as heck; I don't need to cut samples instead I just use a vice, hammer, and file to notch. For additional context, I subjected this material to extended aging treatments at 200C,24hr, 300C,24hr, 400C,24hr, and 500C,24hr. Images from the 200C and 500C aging treatments are included. The 200C image looks like bainite of some form- a vilella etch brings out the plates better. The 500C image looks like fine-pearlite. The treatments in the 200-400C range had a similar bainitic appearance. I'm stumped on the as-received microstructure because it doesn't resemble ausferrite as I know it. I would like to get a second opinion.

Thanks




As-Recieved:
ADI_28-HRC_Austempered_eh5aau.png


200C/24hr:
ADI_28-HRC_200C_24hr_Austempered_c6kctf.png


500C/24hr:
ADI_28-HRC_500C_24hr_Austempered_uihbb0.png
 
Replies continue below

Recommended for you

Sort by date Sort by votes
What hardness did you measure after each of the heat treatments?
 
Upvote 0 Downvote
mrfailure:

No change in hardness (HRC) until 500C. The hardness dropped a 2 points. I know the as-received hardness isn't what you want in an austempered ductile iron. Should be between 35-45 HRC- preferably above 40 HRC in a wear application. I've had other batches where the microstructure had that characteristic lathe appearance.
 
Upvote 0 Downvote
I would second that the as-received is unlikely an ausferrite, but rather more likely a bainite structure. due to
1. lack of ductility
2. hardness sluggish to additional tempering (aging), meaning cementite is already formed in the matrix.
would check if the cooling rate was not high enough at austempering, and/or the temperature was too high (up to 400C?)
 
Upvote 0 Downvote
Thanks MagBen,

Superpicral etch also shows massive carbides for the as-received:

ADI_28-HRC_superpicral_acx2pc.png


This seems to be somewhere between ausferrite and bainite because additional heat treatment at 200C, 24hr produces the "typical" bainite structure. I think an SEM analysis will be informative. From a practical level, this material is unusable, but I would still like to understand how this microstructure evolves with heat treatment.
 
Upvote 0 Downvote
I haven't worked with these for decades but too slow of cooling would be my first thought.
Places that do a lot of ADI have their own special chemistries in order to make HT easier and more consistent.

= = = = = = = = = = = = = = = = = = = =
P.E. Metallurgy, consulting work welcomed
 
Upvote 0 Downvote
Status
Not open for further replies.

Similar threads

mrmalcolm
  • Locked
  • Question
ductile - brittle transition temperature for welded joints
Replies
2
Views
218
EdStainless
EdStainless
Tmoose
  • Locked
  • Question
ASTM A48 cast iron test bar size
Replies
2
Views
284
casting supplier
casting supplier
Robertsolo
  • Locked
  • Question
Would like to strengthen iron electroform
Replies
1
Views
109
EdStainless
EdStainless
hirschaplin
  • Locked
  • Question
Compressor casing in Spheroidal graphite cast iron and impact testing
Replies
2
Views
224
EdStainless
EdStainless
Tmoose
  • Locked
  • Question
modifying ASTM A536 ductile iron standard material Grades
Replies
3
Views
193
Martinos
Martinos

Part and Inventory Search

Sponsor

Back
Top Bottom